7075 aluminum alloy is a cold-treated forging alloy with high strength, far better than mild steel. 7075 aluminum alloy wire is one of the most powerful alloys wires for commercial use. Zinc is the main alloying element in 7075. Adding magnesium to an alloy containing 3%-7.5% zinc can form MgZn2 with remarkable strengthening effect, which makes the heat treatment effect of the alloy far better than the aluminum-zinc binary alloy. 7075 materials are generally added with a small amount of copper, chromium and other alloys. Among them, 7075-T651 aluminum alloy is especially top grade. It is known as the best product in aluminum alloy, with high strength and far better than any mild steel. This alloy has good mechanical and anodic reaction. Representative applications include aerospace, mold processing, mechanical equipment, fixtures, and especially for the manufacture of aircraft structures and other high-stress structures that require high strength and corrosion resistance.


 
The company's 7075 aluminum alloy wire performance
Tensile strength: 524Mpa
0.2% yield strength: >455Mpa
Modulus of elasticity E: >71GPa
Hardness: >150HB
Density: 2.81g/cm^3
 
The company's 7075 aluminum alloy wire product features
1. High strength heat treatable alloy.
2. Good mechanical properties.
3. Good usability.
4. Easy to process and good wear resistance.
5.T7351 state enhances corrosion crack resistance
6. High strength materials for high pressure structural parts.